SF-2X Boundary Lubricated Bearing for Low-Speed Applications

SF-2X boundary lubricated bearing is based on steel plate, with sintered spherical bronze powder in the middle, modified polyoxymethylene (POM) rolled on the surface, and contains oil storage pits. It is suitable for low-speed and medium-load places under normal temperature conditions, replacing traditional copper sleeves, which not only reduces costs but also prolongs service life. In special cases, it can be used on rolling mills to save refueling frequency and simplify replacement procedures. This product has been widely used in automobile chassis, forging machine tools, metallurgical mining machinery, engineering machinery, hydropower, rolling steel industry and other fields.

Mendapatkan sebut harga

PREV：SF-2Y Boundary Lubricated Lead-free Bearing NEXT：SF-PK PEEK Triple Composite Bearing

pengenalan produk
Parameter
Keterangan Bahan
Hubungi Kami

Ciri-ciri Produk

1 Boleh bekerja untuk masa yang lama dalam keadaan bebas minyak.

2 Lebih sesuai untuk keadaan kerja berkelajuan rendah dan beban berat, dengan rintangan haus yang baik dan geseran yang sangat rendah.

3 Sesuai untuk situasi di mana filem minyak sukar dibentuk, seperti berbalas, berputar dan pergerakan terputus-putus.

4 Tahan kakisan dan pengoksidaan.

5 Bebas penyelenggaraan dan hayat perkhidmatan yang panjang.

Kenapa Pilih Bearing Tanpa Minyak

Kurangkan kos Pembuatan

Tidak perlu peranti bekalan minyak, lubang suntikan minyak atau minyak pemprosesan alur, yang boleh menjimatkan kos pembuatan.

Kurangkan Kos Operasi

Ia sangat mengurangkan penggunaan minyak pelincir, mengurangkan penyelenggaraan peralatan, dan mengelakkan bahaya tersembunyi yang disebabkan oleh bekalan minyak yang tidak mencukupi, mengurangkan dengan berkesan kos operasi.

Memendekkan Masa Reka Bentuk

Reka bentuk bebas minyak memudahkan struktur produk dan menjimatkan masa reka bentuk dengan berkesan. Kami profesional Pembekal ODM bagi SF-2X Boundary Lubricated Bearing for Low-Speed Applications

Kondusif Kepada Perlindungan Alam Sekitar

Tiada kitar semula sisa minyak diperlukan, yang juga bermanfaat untuk perlindungan alam sekitar.

Medan Aplikasi

Suhu tinggi

· Kilang keluli

· Relau peleburan

· Peralatan pengeringan

· Ketuhar pembakar

· Pengawal haba

Kalis air

· Pintu empangan

·Pam air

· Struktur suis cecair

· Struktur luar pesisir

· Peralatan mesin dok dan kelodak

Industri kimia

· Kilang kimia

· Peralatan penyaduran elektrik

·Peralatan rawatan air sisa

· Jentera pencelupan

· Peralatan penapisan minyak dan kimia

Tenaga

·Kuasa angin

· Tenaga baharu

kapal

· Kren dek

· Sauh

· Penutup menetas

· Lengan kemudi

· Jentera pengangkat dan peralatan cincin angkat

Pembuatan Automobil

· Acuan setem

· Struktur kimpalan

· Mengecat dan mengeringkan garisan

· Tali pinggang penghantar logam

·Peralatan mesin

Industri berat

· Jentera kilang paip keluli

· Kilang tayar dan kertas

·Jana kuasa

·Menyambung togol jentera suntikan acuan

Pembinaan, Perlombongan, Pemuatan

· Pembancuh, pengisar, penumbuk

· Jentera pembinaan

· Peralatan perlombongan

·Menyambung galas rod

Jambatan dan Rel Angkat

· Galas jambatan

·Rasuk, jambatan, jambatan gantung

·Reaktor berkaitan tenaga nuklear

·Penjana wap

Technical Parameters

●Maximum bearing pressure: 70N/mm2
●Applicable temperature range: -40~+130℃
●Maximum sliding speed: 2.5m/s
●Friction coefficient: 0.05~0.25
●Maximum allowable PV value (dry): 2.8N/mm2 .m/s
●Maximum allowable PV value (oil): 22N/mm2 .m/s

Metallographic Structure and Material Structure

①Polyoxymethylene and lead mixture 0.3~0.5mm
②Spherical bronze powder 0.2~0.3mm
③Steel back 0.4~2.2mm
④Electroplated layer: Copper layer thickness 0.008mm

Application Features

●Good load bearing and good wear resistance.
●Suitable for rotating motion and swinging motion under high load and low speed, and occasions where frequent opening and closing under load make it difficult to form fluid dynamic lubrication.
●Under boundary lubrication conditions, it can be maintained without oiling for a long time, and oiling in the transition layer can make the bearing service life longer.
●The surface plastic layer can leave a certain margin during processing and molding, and can be processed by itself after assembly and pressing into the seat hole to achieve better assembly size.
●The products are mainly used in automobile chassis, metallurgical machinery, mining machinery, water conservancy machinery, construction machinery, agricultural machinery, rolling equipment, etc.

Chemical Properties

Model	Air	Vacuum	Water	Steam	Weak acid	Medium acid	Strong acid	Alkaline solution
SF-2X	good	good	good	good	poor	N/A	N/A	good

MMD-10 End Surface Friction and Wear Test

Model	Test Duration	Test Conditions			Friction Coefficient	Final Temperature	Final Wear Amount
Model	Test Duration	Lubrication Type	Speed	Pressure	Friction Coefficient	(℃)	(mm)
SF 2X	3hr	Grease	0.4m/s	3.5N/mm2	0.071	40	0.006

Komposisi dan Sifat Bahan
bahan	CuZn25Al5Mn3Fe3	CuSn5Pb5Zn5	CuAl10Ni5Fe5	CuSn12	CuZn25Al5Mn4Fe3
Ketumpatan	8.0	8.9	7.8	8.9	8.0
Kekerasan HB	>210	>70	>150	>95	>250
Kekuatan Tegangan N/mm²	>750	>200	>600	>260	>800
Kekuatan Hasil N/mm²	>450	>90	>260	>150	>450
Pemanjangan%	>12	>15	>10	>৪	>800
Pekali Pengembangan Linear 10 ^-5 / ℃	1.9	1.8	1.6	1.8	1.9
Hadkan Suhu ℃	-40~ 300	-40~ 400	-40~ 400	-40~ 400	-40~ 150
Maks. Muatkan N/mm²	100	60	50	70	120
Maks. Kelajuan (Kering) m/min	15	10	20	10	15
Max.PV N/mm²*m/min	200	60	60	80	200
Mampatan Ubah Bentuk Kekal 300N/mm²	<0.01	<0.05	<0.04	<0.05	<0.05
*Permintaan besar dengan bahan khas disediakan.

Pertukaran Bahan Asas
Kod Bahan	Jenama China GB1176-87	Antarabangsa ISO 1338	Jerman DIN	Jepun JIS	Amerika ASTM(UNS)	England BS	Itali JM	Syarat yang berkenaan
JDB Tuang Gangsa	ZCuZn25AI5 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 C86300	HTB2	JM18-1	Beban tinggi, kelajuan rendah Biasa digunakan
JDB-1Gangsa	ZCuSn5 Pb5Zn5	GKuPb5 Sn5Zn5	DIN1705 G-CuSn5ZnPb	H5111 BC6	B30-92 C83600	LG2	JM7-15	Beban pertengahan, kelajuan rendah Biasa digunakan
JDB-2Gangsa	ZCuAI9Fe4 Ni4Mn2	GCuAI10 FeNiS	DIN17656 G-CuAI10Ni	H5114 AIBC3	B30-92 C95500	AB2	JM3-15	Beban pertengahan, kelajuan pertengahan, Biasa digunakan
JDB-3Gangsa	ZCuSn12		G-CuSn12	CAC503B	B30-92 C90800	PB2	JM1-15	Beban pertengahan, kelajuan rendah, Biasa digunakan
JDB-5	ZCuZn25AI6 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 C86300	HTB2	JM18-1	Lebih beban tinggi, kelajuan rendah, Beban tinggi digunakan

Pelincir Pepejal
Minyak pelincir	ciri-ciri	Aplikasi biasa
SL1 Tambah grafit	Rintangan yang sangat baik terhadap bahan kimia serangan dan geseran rendah, Had Suhu 400 ℃	Sesuai untuk mesin am dan di bawah atmosfera
SL4 tambah PTFE	Terendah dalam geseran dan kebaikan air Pelinciran, Had Suhu 300 ℃	Kapal, turbin hidraulik, turbin gas, dll.

SUBMIT

Tentang kita

Zhejiang Mingxu Machinery Manufacturing Co., Ltd. dahulunya dikenali sebagai Kilang Jentera Jiashan Mingxu Precision, telah diasaskan pada tahun 2011. Syarikat ini terletak di kawasan pedalaman Zon Demonstrasi Pembangunan Bersepadu Delta Sungai Yangtze, dengan lokasi dan pengangkutan yang mudah. Dengan lebih daripada sepuluh tahun pengalaman pembuatan dan R&D, syarikat itu telah terlibat secara mendalam dalam pembangunan dan pengeluaran galas pelincir pepejal, papan selaju, laluan gelongsor dan peluncur. Pembekal ODM dan Syarikat JFB Shoulder Bushing Flange Graphite Inlaid Self-Lubricating Bearing di China. Pembuatan produk menggunakan peralatan automasi moden, melaksanakan standard sistem pengurusan kualiti ISO2000 dengan ketat, dan proses utama diproses oleh mesin CNC berketepatan tinggi. Produk utama syarikat meliputi beberapa siri produk seperti galas pelincir diri bertatah pepejal JDB, galas tersinter keluli-kuprum, galas pelincir sendiri SF-1, galas pelincir sendiri sempadan SF-2 dan galas tembaga FB090. Digunakan secara meluas dalam industri automobil, jentera pembinaan, peralatan metalurgi, jentera perlombongan, pengacuan suntikan, acuan, tekstil, percetakan dan banyak lagi bidang pembuatan jentera; Sehingga kini, produk syarikat telah tersebar di seluruh China dan dieksport ke banyak negara asing, dan amat diiktiraf dan disayangi oleh pelanggan domestik dan asing. Jentera Mingxu mematuhi prinsip perkhidmatan "perkhidmatan berkualiti tinggi yang berorientasikan kualiti", dan berusaha untuk menyediakan pelanggan dengan produk dan perkhidmatan profesional. Bekalan Borong MXB-JFB Shoulder Bushing Flange Graphite Inlaid Self-Lubricating Bearing. Syarikat akan terus memperkenalkan bakat, menambah baik mekanisme pengurusan, integriti, pembangunan, inovasi, dan berusaha untuk membina jenama bertaraf dunia.